Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Luran® S 757G - ASA - INEOS Styrolution

Material Data Center offers the following functions for Luran® S 757G:
unit conversion, PDF datasheet print, comparison with other plastics, application examples, snap fit calculation, beam deflection calculation, parameters for material models, CAE Interfaces

Check here, which other Luran S datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
제품 설명서
Particularly easy flowing injection moulding grade for difficult mouldings with large flow path/wall thickness ratios.
Processing/Physical Characteristics단위시험규격
ISO 데이터
용융 부피 - 흐름 속도, MVR 25 cm³/10min ISO 1133
온도 220 °C -
하중 10 kg -
성형 수축률, 평행 0.5 % ISO 294-4, 2577
성형 수축률, 수직 0.9 % ISO 294-4, 2577
이형온도 95 °C -
기계적 특성단위시험규격
ISO 데이터
인장탄성률 2400 MPa ISO 527
항복강도 51 MPa ISO 527
항복변형률 3.3 % ISO 527
파단시 평균신율 8 % ISO 527
탄성변형률, 1h 2200 MPa ISO 899-1
탄성변형률, 1000h 1650 MPa ISO 899-1
챠피 충격 강도 , +23°C 190 kJ/m² ISO 179/1eU
챠피 충격 강도, -30°C 80 kJ/m² ISO 179/1eU
챠피 노치드 충격 강도, +23°C 12 kJ/m² ISO 179/1eA
챠피 노치드 충격 강도, -30°C 3 kJ/m² ISO 179/1eA
열적 특성단위시험규격
ISO 데이터
하중하에서의 변형온도, 1.80 MPa 96 °C ISO 75-1/-2
하중하에서의 변형온도, 0.45 MPa 101 °C ISO 75-1/-2
비카트 연화 온도, B 97 °C ISO 306
선형 열팽창 계수, 평행 95 E-6/K ISO 11359-1/-2
1.5mm 평균두께에서의 난연성 HB class IEC 60695-11-10
테스트 두께 1.6 mm -
Yellow Card 유효한 - -
두께 H인 제품의 난연성 HB class IEC 60695-11-10
테스트 두께 0.8 mm -
Yellow Card 유효한 - -
산소지수로서의 난연성 19 % ISO 4589-1/-2
전기적 특성단위시험규격
ISO 데이터
상대 유전율, 100Hz 3.4 - IEC 62631-2-1
상대 유전뮬, 1MHz 3.2 - IEC 62631-2-1
소산 인자, 100Hz 100 E-4 IEC 62631-2-1
소산 인자, 1MHz 250 E-4 IEC 62631-2-1
부피 저항 1E12 Ohm*m IEC 62631-3-1
표면 저항 1E13 Ohm IEC 62631-3-2
전기 압력 35 kV/mm IEC 60243-1
CTI 600 - IEC 60112
기타 특성단위시험규격
물에서의 흡수성 1.65 % ISO 62와 유사
조건에서의 흡습성 0.35 % ISO 62와 유사
밀도 1070 kg/m³ ISO 1183
테스트 견본 생산단위시험규격
ISO 데이터
사출성형: 용융수지온도 250 °C ISO 294
사출성형: 금형온도 60 °C ISO 294
사출성형: 사출속도 200 mm/s ISO 294
Processing Recommendation Injection Molding단위시험규격
Pre-drying - Temperature 80 °C -
Pre-drying - Time 2 - 4 h -
용융수지온도 240 - 280 °C -
성형온도 40 - 80 °C -
도표
점도-변형률 , Luran® S 757G, ASA, INEOS Styrolution
전단-변형률 , Luran® S 757G, ASA, INEOS Styrolution
응력-신율 , Luran® S 757G, ASA, INEOS Styrolution
시컨트탄성율-신율 , Luran® S 757G, ASA, INEOS Styrolution
응력-신율(등시) 23°C, Luran® S 757G, ASA, INEOS Styrolution
크립탄성율-시간 23°C, Luran® S 757G, ASA, INEOS Styrolution
곡선 크리프 23°C, Luran® S 757G, ASA, INEOS Styrolution
응력-신율(등시) 60°C, Luran® S 757G, ASA, INEOS Styrolution
크립탄성율-시간 60°C, Luran® S 757G, ASA, INEOS Styrolution
곡선 크리프 60°C, Luran® S 757G, ASA, INEOS Styrolution
비용적-온도(pvT) , Luran® S 757G, ASA, INEOS Styrolution
인장탄성율-온도 , Luran® S 757G, ASA, INEOS Styrolution
특징
생산 공정
사출 성형
인도 유형
펠렛 (입자,알갱이)
부가물
이형제
특별 특성
가시광선 안정성, U.V. 안정성 또는 기후 안정성, 열안정성
지역별 검색
기타 정보
사E성
PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
injection molding, Melt temperature, range: 240 - 280 °C
injection molding, Melt temperature, recommended: 250 °C
injection molding, Mold temperature, range: 40 - 80 °C
injection molding, Mold temperature, recommended: 60 °C
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.